SEPTON™ High Performance Thermoplastic Rubber |
| These are typical values and should not be used to set specifications.
(Tested by KURARAY CO., LTD.) |
Type
|
Grade
|
Styrene
Content
wt% |
Specific
Gravity |
Hardness
shoreA |
Tensile Property |
MFR |
Solution Viscosity |
|
100%
Modulus
MPa |
Tensile
Strength
MPa |
Elongation
% |
230˚C
2.16kg
g/10min |
200˚C
10kg
g/10min |
|
5wt%
mPa·s |
10wt%
mPa·s |
15wt%
mPa·s |
|
Physical
Form1) |
| SEP |
1001 |
35 |
0.92 |
80 |
- |
2 |
<100 |
|
|
Pellet |
| 1020 |
36 |
0.92 |
70 |
- |
1.2 |
<100 |
|
|
Powder |
| SEPS |
2002 |
30 |
0.91 |
80 |
3.2 |
11.2 |
480 |
|
|
Pellet |
| 2004 |
18 |
0.89 |
67 |
2.2 |
16 |
690 |
|
|
Pellet |
| 2005 |
20 |
0.89 |
- |
- |
- |
- |
|
|
Powder |
| 2006 |
35 |
0.92 |
- |
- |
- |
- |
|
|
Powder |
| 2007 |
30 |
0.91 |
80 |
3.0 |
16.7 |
580 |
|
|
Pellet |
| 2063 |
13 |
0.88 |
36 |
0.4 |
10.8 |
1200 |
|
|
Pellet |
| 2104 |
65 |
0.98 |
98 |
- |
4.3 |
<100 |
|
|
Pellet |
| SEEPS |
4033 |
30 |
0.91 |
76 |
2.2 |
35.3 |
500 |
|
|
Powder |
| 4044 |
32 |
0.91 |
- |
- |
- |
- |
|
|
Powder |
| 4055 |
30 |
0.91 |
- |
- |
- |
- |
|
|
Powder |
| 4077 |
30 |
0.91 |
- |
- |
- |
- |
|
|
Powder |
| 4099 |
30 |
0.91 |
- |
- |
- |
- |
|
|
Powder |
| SEEPS-OH |
HG252 |
28 |
0.90 |
80 |
3.0 |
23 |
500 |
|
|
Pellet |
| SEBS |
8004 |
31 |
0.91 |
80 |
2.3 |
31.6 |
560 |
|
|
Powder |
| 8006 |
33 |
0.92 |
- |
- |
- |
- |
|
|
Powder |
| 8007 |
30 |
0.91 |
77 |
3.5 |
29 |
550 |
|
|
Powder/Pellet |
| 8076 |
30 |
0.91 |
72 |
1.1 |
2.9 |
530 |
|
|
Pellet |
| 8104 |
60 |
0.97 |
98 |
12.9 |
32.8 |
500 |
|
|
Pellet |
| Measurement Method |
ISO 1183 ISO 48 |
ISO 37 |
ISO 1133 |
Toluene Solution; 30deg.C |
|
|
|
|
|
1)Precautions should be taken in handling and storing. Refer to the appropriate Material Safety Data sheet for further safety information. |
|