Adhesives |
|
Due to their excellent balance of properties and versatility, SEPTON™ polymer are applied to a wide variety of uses as can be seen below. |
| |
SEPTON™ Solubility |
| Poor or Non Soluble In : |
Ethyl Acetate, Methyl Ethylketone,
Methanol, Ethanol, Acetone, Water |
| Soluble : |
Petroleum Ether, Toluene, Benzene,
Hexane, Cyclohexane |
|
| |
Tackifiers Compatible with SEPTON™ |
| Rubber Phase: |
Alicyclic Saturated Hydrocarbon Resins,
Hydrogenated Terpene Resins,
Petroleum Resin, Hydrogenated Rosin Resin |
|
| |
Hot melt Adhesives |
(Tested by KURARAY CO.,LTD.) |
|
| |
1 |
2 |
3 |
4 |
5* |
SEPTON™ 2063
SEPTON™ 2004
SEPTON™ 8076
Tackifier
Paraffinic Process Oil
Antioxidant(parts by wt.) |
100
300
100
1
|
100
250
100
1
|
100
200
100
1
|
100
300
100
1
|
100
300
100
1
|
| Rolling Ball Tack Test |
3 |
18 |
22 |
< 2 |
< 2 |
| Creep Test : |
Holding Power |
(min) |
| |
Slippage |
(mm) |
|
90
|
104
|
105
|
> 240
6.5 |
20
|
| Peel Test : |
To Stainless Steel |
(g/cm) |
| |
To PE |
(g/cm) |
|
1200
1090 |
1000
840 |
740
480 |
1380
500 |
920
810 |
| Melt Viscosity 160˚C | (mPa·s) |
|
3250 |
4280 |
5600 |
4700 |
720 |
|
| TEST Conditions: |
| Coating Thickness: |
30 μm |
| |
15 μm for No.5* |
| Rolling Ball Tack Test: |
JIS Z-0237 Inclined Ball Tack: Measured at 25˚C |
| |
(The higher the number, the higher the tack level) |
Creep Test: Load 1kg at 40˚C, Sample Size 25mm ×25mm
Peel test:180˚ Peel test Rate of Peel 300mm/min at 25˚C
Melt Viscosity:Brook field viscometer |
|
|